Cold Work Steel 2510

Main Characteristic

2510 is a cold work tool steel that is match for heat treatment with oil.
With its unique properties of combination by Carbon and Manganese in the proportion
of 1.0%, this lead to the best quality of hardenability in depth. Besides, 2510 still maintain
hardness after hardening at 64 HRC. It can reach high strength and durability.
Can be used for general purpose at temperature 200 degree celcius. It's good
for application that require hard surface, internal strength after tempering.


OutStanding Properties

Can maintain hardnes of cutting edge
Hardenability in depth. Provide with hardness and strength after heat treatment
Good carbon maintaining properties on surface during heat treatment
Easy on machining
Can do hard chrome after hardening

Application

2510 is widespread selected for Mold that do not require high volume. To name, blanking,
stamping, pressing, coin pressing, bending
Also, blanking mold of workpiece thickness less than 4 mm application. Mold parts that require
high strength. Wood/plastic drilling tool Cutting tool for Plastic/wood Broaches high precision
tool Plastic mold


C Mn Cr V W
0.95 1.1 0.6 0.1 0.6  
Chemical Composition
ส่วนผสมทาง เคมี (%wt.)
AISI
JIS
DIN
สภาพจําหน่าย Selling Condition
สภาพหลังชุบ After Quenching
O1
SKS-3
1.2510 / 100MnCrW4
อบอ่อน ความแข็งสูงสุด 230 HB
ชุบแข็งและอบคืนตัว 58-64 HRC
2510 คุณสมบัติทั่วไป (General Characteristic)